Specification

AISI 52100, 100Cr6, 1.3505, SUJ2, EN31B

Description

· A low alloy chrome steel specifically formulated for use in bearings. 

Material Composition

· Carbon (C) 0.98% to 1.1% 

· Chrome (Cr) 1.45% 

· Silicon (Si) 0.23% 

· Manganese (Mn) 0.35% 

· Posphorous (P) < 0.025% 

· Sulphur (S) < 0.025% 

Mechanical Properties

· Density: 7.81 g cm-1 

· Hardness: 58 to 62 HRC 

· Modulus of Elasticity: 210GPa 

· Shear Modulus: 80GPa 

· Poissons Ratio: 0.3 

· 

Electrical Properties

· Electrical resistivity: 2.19 ?Ohm mm 

Thermal Properties

· Coefficient of thermal expansion @20-300C: 12.00x10-6 K-1 

· Thermal conductivity: 46.6 W m-1 K-1 

Corrosion Resistance

· Low resistence to corrosion, and particularly prone to pitting in damp atmosphereric conditions. 

· Care must be taken to avoid moisture in both use and storage. 

Available Sizes

· 0.5mm (1/64") to 150mm (2") although availability of sizes above 2" is limited 

Available Grades

· AFBMA Std 10: 3, 5, 10, 15, 20, 25, 28, 50, 100, 200, 500, 1000, 2000 

· ISO 3790: 3, 5, 10, 15, 20, 25, 28, 50, 100, 200, 500, 1000, 2000 

· DIN 5401:Class I, Class II, Class III, Class IV, Class V, Class VI 

Applications

· Ball Bearings, Valves, Measuring Equipment, Ball Screws, 

General Information

· By far the most used ball material, Chrome steel balls provide the most cost effective 
solution for the vast majority of applications